<\/p>\nCasthouse Flux is mainly a mixture of chloride and fluoride salts and other additives. Generally, the covering flux requires a small surface tension and a low melting point; the flux used for slag removal requires a large surface tension for molten aluminum, but a small surface tension for oxidized slag; refining flux is required to have good adsorption capacity for alumina, and at the same time, it also requires a certain dissolving capacity for alumina; for more degassing, it is also hoped that the flux has an appropriate gas generation rate, and so on.<\/p>\n
<\/p>\n
Regarding the production method of Casthouse Flux, it should first depend on the chemical composition of the flux. According to physical properties, fluxes can be divided into two categories: melting flux and volatile flux. Generally, it is best to use the melting method for the production of melting flux, while for the volatile flux or the flux containing volatile components, it is generally produced by the mixing method. The granular flux is produced by the fusion method, which is undoubtedly beneficial to the uniform composition of the flux, the decrease of the melting point, the removal of water, the improvement of fluidity, and the extension of the action time.<\/p>\n
Casthouse Flux Features<\/strong><\/p>\n Within the working temperature range, no chemical reaction harmful to molten aluminum is produced. Choosing the right refining temperature, the amount of refining agent, and the correct adding method can improve the refining effect.<\/p>\n When the refining temperature is increased, the surface tension of the flux is reduced, the wettability of the oxidized inclusions is better, and the adsorption and slag removal effect is stronger. At the same time, the flux\u2019s ability to dissolve inclusions is improved, and the chemical interaction between the flux and the melt is enhanced. As the melt viscosity decreases, the ups and downs of inclusions become easier, so it is beneficial to improve the refining effect.<\/p>\n
\nIt has good refining properties, as well as slagging properties and the required performance of removing metal impurities.
\nThe melting point is lower than the melting temperature, and it has good fluidity in the liquid state.
\nIt is easy to separate from the molten aluminum and does not stick to the furnace wall and tools.
\nThe density is less than the density of molten aluminum at working temperature.<\/p>\n