![\"Cast](\"https:\/\/aluminiumceramicfiber.com\/wp-content\/uploads\/2021\/11\/Cast-Rolling-Production.jpg\")
<\/p>\nCast-rolling production is widely used in aluminum alloy deep-processing production. The cast-rolling production has the advantages of short process flow, low energy consumption, small dendritic distance, and fine intermetallic compounds.<\/p>\n
<\/p>\n
However, in the actual production process, there are various defects in the broken cast-rolled plate, among which the cracked edge is a common defect in the production process.<\/p>\n
The existence of this defect makes the cast-rolling strips continuously subjected to tensile and compressive stresses in the subsequent production process, and the cracked edges continue to expand. In particular, the original large cracked edges spread rapidly during cold rolling, and reaching a certain extent will cause strip breakage, interrupt production.<\/p>\n
In addition, too large cracks cannot be completely cut off, which not only affects the subsequent processing and user use, but also increases the cost. Therefore, it is an urgent problem for production technicians, such as excessive cracking and avoiding the occurrence of cracks during the casting and rolling production process.<\/p>\n
According to the casting-rolling principle, in the casting-rolling zone, the liquid metal is cooled by two rotating rolls, and the two processes of casting and rolling are completed in a short time. There is no relative sliding between the surface of the metal and the surface of the roll, and the rolled piece becomes thinner, and there is only a large back sliding in the center.<\/p>\n
Therefore, the metal surface and the inner layer are deformed under the action of shearing force and pressure, and transferred to the solidified hard shell of the liquid cavity, causing the same deformation and shearing force inside the solidified hard shell.<\/p>\n
When the shear force generated by deformation exceeds the shear strength of the solidified hard-shell metal, the weak part of the material cracks first and then expands. After the stress here is fully relaxed, the crack no longer expands, thus forming a crack.<\/p>\n